Home > Sodium tungstate

Sodium tungstate

Sodium tungstate
CAS number
13472-45-2
Molecular weight
329.86
Molecular formula / chemical symbol
Na2WO4.2H2O

Description

The predominant route to this salt is the extraction of tungsten ores, almost all of which are tungstates. Thus, the ores, are treated with base to give sodium tungstate, as illustrated in the case of wolframite:

Fe/MnWO4 + 2 NaOH + 2 H2O → Na2WO4?2H2O + Fe/Mn(OH)2

Scheelite is treated similarly using sodium carbonate.

Sodium tungstate can also be produced by treating tungsten carbide with a mixture of sodium nitrate and sodium hydroxide in a fusion process which overcomes the high exothermicity of the reaction involved.

Several polymorphs of sodium tungstate are known, three at only one atmosphere pressure. They feature tetrahedral orthotungstate dianions but differ in the packing motif. The WO42- anion adopts a structure like sulfate (SO42-).

Sodium tungstate

IUPAC name[hide]

Sodium tungstate

Identifiers

CAS number

13472-45-2 Y

PubChem

26052

RTECS number

YO7875000

Jmol-3D images

Image 1

Properties

Molecular formula

Na2O4W

Molar mass

293.82 g mol?1

Appearance

white rhombohedral crystals

Density

4.179 g/cm3 (anhydrous)
3.25 g/cm3 (dihydrate)

Melting point

698 °C, 971 K, 1288 °F

Solubility in water

57.5 g/100 mL (0 °C)
74.2 g/100 mL (25 °C)
96.9 g/100 mL (100 °C)

Solubility

slightly soluble in ammonia
insoluble in alcohol, acid

Structure

Crystal structure

rhombic (anhydrous)
orthorhombic (dihydrate)

 Y (verify) (what is: Y/N?)
Except where noted otherwise, data are given for materials in their standard state (at 25 °C, 100 kPa)

USES

For the metal tungsten, tungsten acid and tungstate manufacturing as well as dyes, pigments, inks, such as electroplating.

For fabric and cellulose fire retardant, catalyst, etc.


Keyword:Catalyst;Environmental protection paint


Report